|Minimum Order Quantity||500 Kg|
|Features||Shrinkage compensated,polymer fibre reinforced,thixotropic repair mortar|
|Grade||Industrial Construction Repairs|
|Thickness||A minimum thickness of 10mm must be maintained over the whole repair area|
|Compressive Strength N Per Mm||25 N mm at 1 day 70 N mm at 28 days|
MasterEmaco S 488 is a cementitious pre-bagged ready-to-use structural repair mortar in powder form. When mixed with the correct amount of water, it produces a thixotropic, high strength repair mortar, reinforced with acrylic polymer fibres. It exhibits excellent bond characteristics to steel reinforcement and to concrete.
MasterEmaco S 488 mortar is shrinkage compensated mortar and contains no metallic aggregate and is chloride free. Once the product has cured it has low permeability and is extremely durable.
MasterEmaco S 488 is formulated for sprayed or trowelled applications; in thicknesses up to 50mm in one layer by hand application. Greater thicknesses can be achieved when spray applied.What is MasterEmaco S 488 used for?
MasterEmaco S 488 is designed for all types of structural concrete repair which can be applied by trowel or by spray application:
MasterEmaco S 488may be used in conjunction with MasterEmaco 8100 AP to provide extra protection to reinforcing steel.
MasterEmaco S 488 may be cured using MasterKure 181What are the benefits of MasterEmaco S 488?
MasterEmaco S 488offers the following advantages:
|Minimum Order Quantity||10 Kg|
|Features||Fast setting, Shrinkage compensated Rapid hardening and can be trafficked after 2 hours Good adhesiv|
|Strength||high early & ultimate compressive strength|
MASTER REPAIR KWIK FIX is a ready to use single component rapid hardening, high strength, non shrink repair mortar which requires only addition of clean portable water to produce highly consistent repair mortar. The product is based on blend of portland cement, graded aggregates,fillers, polymers & additives. The mortar when mixed with water it hardens rapidly within 1 hour & can be trafficked after 2 hours. The low water powder ratio of the product ensures for better high early strength development and thus provides long term durabilityFEATURES/ADVANTAGES